CTAB与BDA对45号钢镀锌层耐腐蚀性的影响

王顺, 范海林, 李庆余   

  1. 广西师范大学化学与药学学院,广西桂林541004
  • 收稿日期:2015-08-04 发布日期:2018-09-14
  • 通讯作者: 李庆余(1962—),男,湖南邵东人,广西师范大学教授,博士。E-mail:13975808173@126.com
  • 基金资助:
    国家自然科学基金资助项目(21473042)

Influence of CTAB and BDA on Corrosion Resistance ofZn Coating on the Surface of 45# Steel

WANG Shun, FAN Hailin, LI Qingyu   

  1. School of Chemistry and Pharmaceutical Sciences,Guangxi Normal University,Guilin Guangxi,541004,China
  • Received:2015-08-04 Published:2018-09-14

PDF (PC)

151

摘要： 采用CTAB(十六烷基三甲基溴化铵)与BDA(苄叉丙酮)作为添加剂在45号钢上进行镀锌,研究这2种添加剂对镀锌层耐腐蚀性的影响。通过利用SEM、XRD对镀锌层形貌和晶体结构、晶粒尺寸进行比较,利用塔菲尔极化曲线以及交流阻抗等测试方法对镀锌层耐腐蚀性能进行比较。结果表明,CTAB、BDA的添加改变了镀锌层的表面形貌,晶粒尺寸由微米尺寸变为纳米尺寸,晶面(110)为择优取向,提高了镀层的耐腐蚀性能;同时添加CTAB与BDA所得到的镀层形貌紧凑、平整,耐腐蚀性能最好。

关键词: 45号钢, 镀锌, CTAB, BDA, 耐腐蚀性能

Abstract: Zn coatings were prepared on the surface of 45# steel by using cetyltrimethylammonium bromide and benzalacetone as additives. Influence of the two additives on corrosion resistance of Zn coatings was investigated. The morphology and crystalline structure,grain sizes were characterized by SEM and XRD. The corrosion resistance of the coatings were analyzed by Tafel and EIS tests. The results showed that addition of CTAB and BDA changed the surface morphology and the grain size changed from micron size to nanometer size. Meanwhile,the crystal plane (110) was the crystallographic preferential orientation of Zn coatings and the corrosion resistance of Zn coatings increased. The coatings obtained by adding both CTAB and BDA were more compact and smooth,which enhanced the corrosion resistance of Zn coatings.

Key words: 45# steel, Zn plating, CTAB, BDA, corrosion resistance

中图分类号: 

  • TQ153.1
[1] 安茂忠,李丽波,杨培霞. 电镀技术与运用[M]. 北京:机械工业出版社,2007.
[2] 郭清泉,陈焕钦. 金属腐蚀与涂层防护[J]. 合成材料老化与应用,2004,32(4): 36-39.
[3] 黄盛郎. 镀锌及锌合金发展综述[J]. 电镀与环保,1996,16(2): 3-6.
[4] 高仙芝. 碱性无氰镀锌工艺研究[J]. 火箭推进,2013,39(5): 75-81.
[5] LI G Y,LIAN J S,NIU L Y,et al. Investigation of nanocrystalline zinc-nickel alloy coatings in an alkaline zincate bath[J]. Surface and Coatings Technology,2005,191(1): 59-67.
[6] MURALIDHARA H B,NAIK Y A. Electrochemical deposition of nanocrystalline zinc on steel substrate from acid zincate bath[J]. Surface and Coatings Technology,2008,202(14): 3403-3412.
[7] MURALIDHARA H B,NAIK Y A,VENKATESHA T V. Effect of condensation product of glycyl-glycine and furfural on electrodeposition of zinc from sulphate bath[J]. Bulletin of Materials Science,2006,29(5): 497-503.
[8] MOUANGA M,RICQ L,DOUGLADE J,et al. Corrosion behaviour of zinc deposits obtained under pulse current electrodeposition: effects of coumarin as additive[J]. Corrosion Science,2009,51(3): 690-698.
[9] SABER K,KOCH C C,FEDKIW P S. Pulse current electrodeposition of nanocrystalline zinc[J]. Materials Science and Engineering: A,2003,341(1): 174-181.
[10] RAMANAUSKAS R,QUINTANA P,MALDONADO L,et al. Corrosion resistance and microstructure of electrodeposited Zn and Zn alloy coatings[J]. Surface and Coatings Technology,1997,92(1): 16-21.
[11] 李庆余,范海林,陈家荣,等. 硫脲对304不锈钢镀镍层抗腐蚀性能的影响[J]. 表面技术,2015,44(7): 16-22.
[12] 邬明钰,辛森森,伍玉琴,等. 硫酸盐体系中直流电沉积参数对纳米晶锌镀层的影响[J]. 材料保护,2010,43(8):42-45.
[13] NAYANA K O,VENKATESHA T V. Bright zinc electrodeposition and study of influence of synergistic interaction of additives on coating properties[J]. Journal of Industrial and Engineering Chemistry,2015,26: 549-553.
No related articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] 孟春梅, 陆世银, 梁永红, 莫肖敏, 李卫东, 黄远洁, 成晓静, 苏志恒, 郑华. 岩黄连总碱诱导肝星状细胞凋亡和自噬的电镜实验研究[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 76 -79 .
[2] 李钰慧, 陈泽柠, 黄中豪, 周岐海. 广西弄岗熊猴的雨季活动时间分配[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 80 -86 .
[3] 覃盈盈, 漆光超, 梁士楚. 凤眼莲组织浸提液对靖西海菜花种子萌发的影响[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 87 -92 .
[4] 庄枫红, 马姜明, 张雅君, 苏静, 于方明. 中华水韭对不同光照条件的生理生态响应[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 93 -100 .
[5] 韦宏金, 周喜乐, 金冬梅, 严岳鸿. 湖南蕨类植物增补[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 101 -106 .
[6] 包金萍, 郑连斌, 宇克莉, 宋雪, 田金源, 董文静. 大凉山彝族成人皮褶厚度特征[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 107 -112 .
[7] 林永生, 裴建国, 邹胜章, 杜毓超, 卢丽. 清江下游红层岩溶及其水化学特征[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 113 -120 .
[8] 张茹, 张蓓, 任鸿瑞. 山西轩岗矿区耕地流失时空特征及其影响因子研究[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 121 -132 .
[9] 李贤江, 石淑芹, 蔡为民, 曹玉青. 基于CA-Markov模型的天津滨海新区土地利用变化模拟[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 133 -143 .
[10] 王梦飞, 黄松. 广西西江经济带的城市旅游经济空间关联研究[J]. 广西师范大学学报（自然科学版）, 2018, 36(3): 144 -150 .
版权所有 © 广西师范大学学报（自然科学版）编辑部
地址：广西桂林市三里店育才路15号　邮编：541004
电话：0773-5857325　E-mail: gxsdzkb@mailbox.gxnu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发