介孔二氧化硅制备中粒径和孔径控制研究

周黄歆1,2, 梁振华1,2, 彭桂花1,2, 焦杭州1,2   

  1. 1.广西师范大学 化学与药学学院,广西桂林541004;
    2.广西师范大学 药用资源化学与药物分子工程教育部重点实验室,广西桂林541004
  • 收稿日期:2014-03-07 出版日期:2014-09-25 发布日期:2018-09-25
  • 通讯作者: 梁振华(1978—),男,广西柳州人,广西师范大学研究员,博士。E-mail:liangzh@mailbox.gxnu.edu.cn
  • 基金资助:
    国家自然科学基金资助项目(51102053)

Preparation of Mesoporous Silica Nanoparticles with Controlled Particle Size and Pore Diameter

ZHOU Huang-xin1,2, LIANG Zhen-hua1,2, PENG Gui-hua1,2, JIAO Hang-zhou1,2   

  1. 1.College of Chemistry and Pharmaceutical Science, Guangxi Normal University, Guilin Guangxi 541004, China;
    2. Key Laboratory for the Chemistry and Molecular Engineering of Medicinal Resources, Ministry of Education of China, Guangxi Normal University, Guilin Guangxi 541004, China
  • Received:2014-03-07 Online:2014-09-25 Published:2018-09-25

摘要: 以正硅酸乙酯为硅源,十六烷基三甲基溴化铵作为表面活性剂,研究反应条件如氢氧化钠浓度、反应温度等对介孔二氧化硅颗粒大小和孔径的影响。实验结果表明,在一定范围内,升高反应温度和增加氢氧化钠浓度均使介孔二氧化硅粒径减小,通过添加一定量的三甲苯可以有效增加介孔二氧化硅的孔径。

关键词: 介孔二氧化硅, 粒径可控, 孔径, 正硅酸乙酯, 三甲苯

Abstract: Mesoporous silica nanoparticles with controlled particle sizes and pore diameters were obtained by fine tuning the synthesis parameters. Experimental results showed that mesoporous silica particles with smaller particle size could be obtained at higher reaction temperature and concentration of NaOH. In addition, the pore diameter of mesoporous silica could be expanded by adding of TMB into the reaction solution.

Key words: mesoporous silica, size controllable, pore size, TEOS, TMB

中图分类号: 

  • O611.4
[1] KRESGE C T, LEONOWICZ M E, ROTH W J, et al. Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism[J]. Nature, 1992, 359:710.
[2] BECK J S, VARTULI J C, ROTH W J, et al. A new family of mesoporous molecular sieves prepared with liquid crystal templates[J]. J Am Chem Soc, 1992, 114:10834.
[3] ZHAO Dong-yuan, GOLDFARB D. Synthesis of mesoporous manganosilicates:Mn-MCM-41, Mn-MCM-48 and Mn-MCM-L[J]. J Chem Soc, Chem Commun, 1995(8):875-876.
[4] DIRENZO F, CAMBON H, DUTARTRE R. A 28-year-old synthesis of micelle-templatted mesoporous silica[J]. Microporous Mater, 1997, 10:283-286.
[5] KIM E, KIM H E, LEE S J, et al. Reversible solid optical sensor based on acyclic-type receptor immobilized SBA-15 for the highly selective detection and separation of Hg(Ⅱ) ion in aqueous media[J]. Chem Commun, 2008, 33:3921-3923.
[6] ZHOU Peng, MENG Qing-tao, HE Guang-jie, et al. Highly sensitive fluorescence probe based on functional SBA-15 for selective detection of Hg2+ in aqueous media[J]. J Environ Monit, 2009, 77:648-653.
[7] LIN V S Y, LAI Cheng-yu, HUANG Jian-guo, et al. Molecular recognition inside of multifunctionalized mesoporous silicas:toward selective fluorescence detection of dopamine and glucosamine[J]. J Am Chem Soc, 2001, 725:11510-11511.
[8] RODMAN D L, PAN Hong-jun, CLAVIER C W, et al. Optical metal ion sensor based on diffusion followed by an immobilizing reaction. Quantitative analysis by a mesoporous monolith containing functional groups[J]. Anal Chem, 2005, 77:3231-3237.
[9] KIM J, KIM H S, LEE N, et al. Multifunctional uniform nanoparticles composed of a magnetite nanocrystal core and a mesoporous silica shell for magnetic resonance and fluorescence imaging and for drug delivery[J]. Angew Chem Int Ed, 2008, 47:8438-8441.
[10] YAMADA H, URATA C, UJIIE H, et al. Preparation of aqueous colloidal mesostructured and mesoporous silica nanoparticles with controlled particle size in a very wide range from 20 nm to 700 nm[J]. Nanoscale, 2013, 5:6145-6153.
[11] HUO Qi-sheng, SCHUTH F, STUCKY G D, et al. Preparation of hard mesoporous silica spheres[J]. Chem Mater, 1997, 9:14.
[12] FENG Jiang-lin, HUO Qi-sheng, MELOSH N, et al. Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores[J]. Science, 1998, 279:548-552.
[13] SHIBA K, SHIMURA N, OGAWA M, et al. Mesoporous silica spherical particles[J]. J Nanosci Nanotechno, 2013, 13:2483-2494
[14] WU Si-han, MOU Chung-yuan, LIN Hong-ping. Synthesis of mesoporous silica nanoparticles[J]. Chem Soc Rev, 2013, 42: 3862-3875.
[15] FUERTES A B, VALLE-VIGON P, SEVILLA M. Synthesis of colloidal silica nanoparticles of a tunable mesopore size and their application to the adsorption of biomolecules[J]. J Colloid Interface Sci, 2010, 349:173-180.
[1] 王晓凤, 王夏, 彭桂花, 梁振华, 吴京隆. 硅钼比对核壳结构SiO2/CaMoO4:Eu3+,Li+红色荧光粉的影响[J]. 广西师范大学学报(自然科学版), 2013, 31(4): 84-87.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 广西师范大学学报(自然科学版)编辑部
地址:广西桂林市三里店育才路15号 邮编:541004
电话:0773-5857325 E-mail: gxsdzkb@mailbox.gxnu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发