广西师范大学学报（自然科学版） ›› 2012, Vol. 30 ›› Issue (3): 171-177.

• • 上一篇    下一篇

刚性柱双π墙金属有机框架:单晶到单晶结构转换,碘富集与缓释,协同导电性研究

曾明华, 李丹丹, 殷政, 王强心, 张东材   

  1. 广西师范大学化学化工学院,广西桂林541004
  • 收稿日期:2012-06-20 出版日期:2012-09-20 发布日期:2018-12-04
  • 通讯作者: 曾明华(1972—),男,湖南邵阳人,广西师范大学教授,博导。E-mail:zmh@mailbox.gxnu.edu.cn
  • 作者简介:曾明华,男,1972年生,湖南邵阳人,博士,现任广西师范大学化学化工学院教授,无机化学专业博士生导师。
  • 基金资助:
    国家自然科学基金资助项目(20871034);广西自然科学基金资助项目(00832001Z,GKN0630006-5D);教育部“新世纪优秀人才支持计划”资助项目(NCET-07-217);广西新世纪十百千人才工程第二层次人选资助项目(2006201)

Rigid Pillars and Double Walls in a Porous Metal-Organic Framework: Single-Crystal to Single-Crystal,Controlled Uptake and Release of Iodine and Electrical Conductivity

ZENG Ming-hua, LI Dan-dan, YIN Zheng, WANG Qiang-xin, ZHANG Dong-cai   

  1. College of Chemistry and Chemical Engineering,Guangxi Normal University,Guilin Guangxi 541004,China
  • Received:2012-06-20 Online:2012-09-20 Published:2018-12-04

摘要： 本文在溶剂热条件下利用刚性柱型金属手性配位链(Zn-lactate),辅助于三角架桥联配体(pybz)构筑了目前第一例高稳定性、双π墙的纳米孔道配位聚合物Zn3(pybz)2(lac)2·2.5DMF(1)。化合物1具有孔径为1.12 nm× 1.02 nm的一维纳米通道,其孔洞率Vvoid为43.5%,Langmuir比表面积为918.5 m2·g-1,热稳定性高达400 °C。化合物1通过晶态转换的方式得到去客体化合物Zn3(pybz)2(lac)2(1′)。1′在碘的环己烷溶液中展现出对碘分子前所未有的超级富集与控释效果,单位碘负载量达到1 g I2/g 1′,同时载碘单晶在乙醇溶液中可实现碘的可控释放。由于客体I2分子与主体双壁π电子两者间交替的电荷转移,导致载碘单晶的导电性能比碘单质剧增440倍。上述研究,在国际上首次发现了绝缘性客体与绝缘性配位聚合物主体协同有序电荷转移进而导电性剧增的特殊现象。

关键词: 金属有机框架, 单晶到单晶结构转换, 碘富集与缓释, 协同导电性

Abstract: The first high stable micro-porous metal-organic framework with rigidpillars and double-walls,Zn3(pybz)2(lac)2·2.5DMF (1) wasconstructed from infinite pillars {[Zn3(DL-lac)2]2+}n and 4-pyridyl benzoate(pybz) which is long,polar and ditopic at the opposite ends through the pyridine and the carboxylate under solvothermal reaction.1 crystallized in tetragonal P4—21c space group.Thereare 1D channels running along the c axis with window size of 1.12×1.02 nm2 in 1.A void volume of 43.5% was calculated by PLATON.A Langmuir surface area of918.5 m2·g-1 further confirms the permanent porosity of complex 1′.The framework of 1 is highly stable up to 400 °C which is confirmed by TG and variable temperature powder X-ray diffraction measurement.Guest removed phase Zn3(pybz)2(lac)2 (1′) can be obtained through single-crystal to single-crystal transformation.1′ shows outstanding iodine enrichment ability in cyclohexanesolution of I2and one gram of 1′ can absorb approximately 1 g of iodine to obtain {[Zn3(pybz)2(lac)2]·3I2}n (1′·3I2).1′·3I2 shows controlled iodine releasing in ethanol solvent.The potential intermolecular interactions between I2 and π-electronwalls induced n→σ* charge-transfer and resulted in cooperative electrical conductivity for of 1′ 3I2,which is about 440 times higher than iodine.A special phenomena was found that increased electrical conductivityresulted from cooperative interaction between insulating guests and insulating coordination polymers for the first time.

Key words: metal-organic framework, single-crystal to single-crystal transformation, iodine enrichment and controlled releasing of iodine, cooperative electrical conductivity

中图分类号: 

  • O641
[1] YAGHI O M,FURUKAWA H.Storage of hydrogen,methane,and carbon dioxidein highly porous covalent organic frameworks for clean energy applications[J].J Am Chem Soc,2009,131(25):8875-8883.
[2] CZAJA A U,TRUKHAN N,MÜLLER U.Industrial applications of metal-organic frameworks[J].Chem Soc Rev,2009,38(12):1284-1293.
[3] KUPPLER R J,ZHOU Hong-cai.Selective gas adsorption and separation in metal-organic frameworks[J].Chem Soc Rev,2009,38(13):1477-1504.
[4] BATTEN S R,NEVILLE S M,TURNER D R.Coordination polymers design,analysis and application[M].London:The Royal Society of Chemistry,2009.
[5] KURMOO M.Magnetic metal-organic frameworks[J].Chem Soc Rev,2009,38:1353-1379.
[6] TRANCHEMONTAGNE D J,MENDOZA-CORTE′S J L,YAGHI O M,et al.Secondary building units,nets and bonding in the chemistry of metal-organic frameworks[J].Chem Soc Rev,2009,38:1257-1283.
[7] HORCAJADA P,SERRE C,MAURIN G,et al.Flexible porous metal-organicframeworks for a controlled drug delivery[J].J Am Chem Soc,2008,130(21):6774-6780.
[8] KATHRYN M L,ROCCA J D,LIN Wen-bin,et al.Postsynthetic modifications ofiron-carboxylate nanoscale metal-organic frameworks for imaging and drug delivery[J].J Am Chem Soc,2009,131(40):14261-14263.
[9] FANG Qian-rong,ZHU Guang-shan,QIU Shi-lun,et al.Mesoporousmetal-organic framework with rare etb topology for hydrogen storage and dye assembly[J].Angew Chem,Int Ed,2007,46(35):6638-6642.
[10] CHAE H K,SIBERIO-PE′REZ D Y,KIM J,et al.A route to high surface area,porosity and inclusionof large molecules in crystals[J].Nature,2004,427:523-527.
[11] DONG Yu-bin,WANG Peng,MA Jian-ping,et al.Coordination-driven nanosized lanthanide “molecular lantern” with tunable luminescent properties[J].JAm Chem Soc,2007,129(16):4872-4873.
[12] ZHAO Bin,CHEN Xiao-yan,CHENG Peng,et al.Coordination polymers containing 1D channels as selective luminescent probes[J].J Am Chem Soc,2004,126(47):15394-15395.
[13] NAKABAYASHI K,KAWANO M,FUJITA M,et al.Cavity-induced spin-spin interaction between organic radicals within a self-assembled coordination cage[J].J Am Chem Soc,2004,126(51):16694-16695.
[14] LAN An-jian,LI Kun-hao,WU Hao-han,et al.A luminescent microporous metal-organic framework for the fast and reversible detection of high explosives[J].Angew Chem Int Ed,2009,48(13):2334-2339.
[15] SPEK A L.PLATON:A multipurpose crystallographic tool[J].Journal of Applied Crystallography,2003,36:7-13.
[16] ZENG Ming-hua,CHEN Xiao-ming,FENG Xiao-long,et al.A robust microporous 3Dcobalt(Ⅱ) coordination polymer with new magnetically frustrated 2D lattices:single-crystal transformation and guest modulation of cooperative magnetic properties[J].Dalton Trans,2006:5294-5303.
[17] ZENG Ming-hua,HU Sheng,CHEN Qing,et al.Apical ligand substitution,shape recognition,vapor-adsorption phenomenon,and microcalorimetry for apillared bilayer porous framework that shrinks or expands in crystal-to-crystal manners upon change in the cobalt(Ⅱ) coordination environment[J].Inorg Chem,2009,48(15):7070-7079.
[18] PAN Long,PARKER B,HUANG Xiao-ying,et al.Zn(tbip) (H2tbip=5-tert-butyl isopthalic acid):a highly stable guest-free microporous metal organic framework with unique gas separation capability[J].J Am Chem Soc,2006,128(13):4180-4181.
[19] OUELLETTE W A,WHITENACK V K,DUNBAR K R,et al.A Thermally andhydrolytically stable microporous framework exhibiting single-chain magnetism:structure and properties of [Co2(H0.67bdt)3]·20H2O[J].Angew Chem Int Ed,2009,48(12):2140-2144.
[20] CHESTER A W,CLEMENT P,HAN S.Faujasite zeolitic materials:USA,200016136291A[P].2000-10-24.
[21] KITAGAWA S,MATSUDA R.Chemistry of coordination space of porouscoordination polymers[J].Coord Chem Rev,2007,251(21):2490-2509.
[22] HU Sheng,HE Kun-huan,ZENG Ming-hua,et al.Crystalline-state guest-exchange and gas-adsorption phenomenon for a “soft” supramolecular porous frameworkstacking by a rigid linear coordination polymer[J].Inorg Chem,2008,47(12):5218-5224.
[23] ZHANG Jie-peng,CHEN Xiao-ming.Optimized acetylene/carbon dioxide sorption in a dynamic porous crystal[J].J Am Chem Soc,2009,131(15):5516-5521.
[24] MURTHI M,SNURR R Q.Effects of molecular siting and adsorbentheterogeneity on the ideality of adsorption equilibria[J].Langmuir,2004,20(6):2489-2497.
[25] GÖRBITZ M,NILSEN K,SZETO LW.Microporous organic crystals:an unusual case for L-leucyl-L-serine[J].Chem Commun,2005,34:4288-4290.
[26] MOHANAMBE L,VASUDEVAN S.Insertion of iodine in a functionalized inorganic layered solid[J].Inorg Chem,2004,43(20):6421-6425.
[27] HERTZSCH T,BUDDE F,WEBER E,et al.Supramolecular-wire confinement of I2 molecules in channels of the organic zeolite tris(o-phenylenedioxy)cyclotriphosphazene[J].Angew Chem Int Ed,2002,41(13):2281-2284.
[28] KURMOO M,LIU Tao,GAO Song,et al.[Fe3(HCOO)6]:A permanent porous diamond framework displaying H2/N2 adsorption,guest inclusion,and guest-dependent magnetism[J].Adv Funct Mater,2007,17(9):1523-1536.
[29] WANG Ze-ming,ZHANG Bin,KURMOO M,et al.Mn3(HCOO)6:a 3D porous magnet ofdiamond framework with nodes of Mn-centered MnMn4 tetrahedron and guest-modulated ordering temperature[J].Chem Commun,2004,4:416-417.
[30] CHOI H J,SUH M P.Dynamic and redox active pillared bilayer open framework:single-crystal-to-single-crystaltransformations upon guest removal,guest exchange,and framework oxidation[J].J Am Chem Soc,2004,126(48):15844-15851.
[31] JACK Y L,BABB A M.A unique eclipsed 2-D coordination polymer with removableiodine molecules in the open-channel structure[J].Chem Commun,2003,12:1346-1347.
[32] ABRAHAMS B F,MOYLAN M,ROBON R,et al.Zinc saccharate:a robust,3D coordination network with two types of isolated,parallel channels,one hydrophilic and the other hydrophobic[J].Angew Chem Int Ed,2003,42(16):1848-1851.
[33] DEBOER G,BURNETT J W,YOUNG M A.Molecular product formation fromthe charge-transfer state of C6H6I2[J].Chem Phys Lett,1996,259:368-374.
[34] SUH M P,CHEON Y E,LEE E Y.Syntheses and functions of porousmetallosupramolecular networks[J].Coord Chem Rev,2008,252(8):1007-1026.
[1] 李历红, 方志刚, 赵振宁, 陈林, 韩建铭, 崔远东, 马填棋, 姜雨晨. 团簇Ni3CoP催化析氢活性研究[J]. 广西师范大学学报（自然科学版）, 2019, 37(1): 165-172.
[2] 李雯博,方志刚,赵振宁,陈 林,徐诗浩,韩建铭,刘 琪,崔远东. 团簇Co5B2反应活性的DFT研究[J]. 广西师范大学学报（自然科学版）, 2017, 35(4): 76-83.
[3] 徐勤, 马超美, 饶伟文, 邓立东. UPLC-QQQMS测定咳特灵中小叶榕干浸膏12种成分[J]. 广西师范大学学报（自然科学版）, 2017, 35(2): 80-86.
[4] 徐诗浩, 方志刚, 韩建铭, 赵振宁, 陈林, 刘琪. 团簇V3B2成键及磁学性质研究[J]. 广西师范大学学报（自然科学版）, 2017, 35(3): 89-96.
[5] 蒋庆科, 邹品田, 罗勇为, 陆海南, 覃江克, 邹华红. QuEChERS-LC-MS/MS法测定黄皮果中30种常用农药残留[J]. 广西师范大学学报（自然科学版）, 2016, 34(3): 109-115.
[6] 黄学仁, 赵志愿, 蒋毅民. 4′-(4-苯甲酸)-2,2′:6′,2″-三联吡啶锌配位聚合物的合成、晶体结构及荧光性质研究[J]. 广西师范大学学报（自然科学版）, 2016, 34(2): 98-104.
[7] 刘汉甫, 马献力, 陈素一, 沈雪松, 黄富平. 锌三元配合物的合成及其抑菌活性研究[J]. 广西师范大学学报（自然科学版）, 2015, 33(4): 103-107.
[8] 蒋丽萍, 黄婉云, 刘冬成, 梁福沛. 水杨醛联二萘酚二甲酰腙Zn(Ⅱ)、Cu(Ⅱ)配合物的合成及晶体结构[J]. 广西师范大学学报（自然科学版）, 2015, 33(1): 93-98.
[9] 霍红月, 李仲庆, 覃其品, 刘延成, 陈振锋. 邻香草醛缩胡椒乙胺席夫碱锌(Ⅱ)配合物的研究[J]. 广西师范大学学报（自然科学版）, 2014, 32(3): 65-73.
[10] 曾建强, 梁光明, 黄瑛达, 杨坤国, 桂柳成, 倪青玲. 氢键导向的三维超分子结构{[Co(4,4'-bipy)(H2O)4](pda)2(H2O)2}n的合成及晶体结构(pda-=2-甲基苯并咪唑-1,3-二乙酸根)[J]. 广西师范大学学报（自然科学版）, 2013, 31(2): 69-75.
[11] 盛良兵, 申艳玲, 熊波皮, 邹华红, 梁福沛. [Mn3(oba)3(DMF)4]配合物的合成、晶体结构及磁学性质[J]. 广西师范大学学报（自然科学版）, 2013, 31(2): 76-80.
[12] 陈思园, 杨扬, 彭艳, 刘延成. 一种新型希夫碱钯配合物的晶体结构及抗肿瘤活性研究[J]. 广西师范大学学报（自然科学版）, 2013, 31(2): 81-86.
[13] 方岳平, 周训富, 杨思源, 王红强. 新颖三维超结构功能材料:SnO2@Carbon核-壳纳米链的合成与储能应用[J]. 广西师范大学学报（自然科学版）, 2012, 30(3): 178-188.
[14] 王修建, 丛新宇, 蒋选丰, 马凯, 张子豪, 曾建强, 倪青玲. 由Au…Au键诱导的Au-有机膦一维配位聚合物的合成、结构及表征[J]. 广西师范大学学报（自然科学版）, 2012, 30(3): 189-193.
[15] 梁福沛, 刘冬成, 聂传丽. [Cd2(BHP)2(2,6-pda)2(H2O)2]·H2O配合物的合成、结构及荧光性质[J]. 广西师范大学学报（自然科学版）, 2012, 30(3): 194-200.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 广西师范大学学报（自然科学版）编辑部
地址：广西桂林市三里店育才路15号　邮编：541004
电话：0773-5857325　E-mail: gxsdzkb@mailbox.gxnu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发