Electrocatalytic Performance of Platinum-modified PAni/PTn Composite Electrode toward Methanol Oxidation

ZHONG Xin-xian, WANG Zhi-hong, YIN Xiao-ling, WANG Yan-jun, HUANGHan-xing, FENG Qi-peng   

  1. Key Laboratory for the Chemistry and Molecular Engineering ofMedicinal Resources,Ministry of Education of China;College of Chemistry and Chemical Engineering,Guangxi Normal University,Guilin Guangxi 541004,China
  • Received:2012-03-29 Published:2018-11-27

摘要: 苯胺(An)与硫堇(Tn)电化学聚合于石墨电极上,并采用电化学方法沉积Pt颗粒,制备得到Pt/PAni-PTn/石墨电极。通过扫描电子显微镜(SEM)对其形貌进行表征,利用循环伏安法(CV)、计时电流法(CA)考察了Pt/PAni-PTn/石墨电极对甲醇的电催化性能。实验结果表明,Pt颗粒均匀地分散在PAni-PTn复合膜上,PAni-PTn载体更有利Pt纳米颗粒的分散和粒径的减小,Pt/PAni-PTn/石墨电极对甲醇的电催化活性和稳定性明显优于Pt/石墨电极。

关键词: Pt, 聚硫堇, 聚苯胺, 甲醇, 电催化氧化

Abstract: Thionine and aniline were polymerized electrochemically at graphite electrode,and Pt particles were deposited by electrochemical method,then Pt/PAni-PTn/graphite electrode was obtained.The morphology of Pt/PAni-PTn/graphite electrode was characterized by scanning electron microscope (SEM).SEM result showsthat Pt particles are dispersed homogeneously on PAni-PTn composite film.The electrocatalytic activity of Pt/PAni-PTn/graphite electrode toward methanol electrooxidation was investigated by cyclic voltammetry (CV) and chronoamperometry (CA).Experimental results show that PAni-PTn as a catalyst support is better forPt to improve its dispersion and reduce its size,showing larger active surfacearea.Pt/PAni-PTn/graphite electrode exhibits better electrocatalytic activityand long-term stability than Pt/graphite electrode.

Key words: Pt, polyaniline, polythionine, methanol, electrocatalytic oxidation

中图分类号: 

  • O614
[1] WEI Yong-sheng,SHEN Liang-bo,WANG Fang-hui,et al.Synthesis andcharacterization of novel nanocomposite membrane of sodium titanate/nafion[J].Mater Lett,2011,65(11):1684-1687.
[2] ZHANG Li-peng,XIA Zhen-hai.Mechanisms of oxygen reductionreaction on nitrogen-doped graphene for fuel cells[J].J Phys Chem C,2011,115(22):11170-11176.
[3] QIU Jian-ding,WANG Guo-chong,LIANG Ru-ping,et al.Controllable deposition of platinum nanoparticles on graphene as an electrocatalystfor direct methanol fuel cells[J].J Phys Chem C,2011,115(31):15639-15645.
[4] LASCH K,HAYN G,JÖRISSEN L,et al.Mixed conducting catalyst support materials for the direct methanol fuel cell[J].J Power Sources,2002,105(2):305-310.
[5] ELENA S R,Francoise Hahn,Nicolas Alonso-Vante.Carbon monoxide oxidation as a probe for PtRu particle surface structure[J].J Phys Chem C,2008,112(47):18521-18530.
[6] SUN Jing-yu,HUANG Jian-shu,CAO Yan-xia,et al.Hydrothermal synthesis of Pt-Ru/MWCNTs and its electrocatalytic properties for oxidation of methanol[J].Int J Electrochem Sci,2007,2(1):64-71.
[7] YUN Ju-mi,KIM Hyung-Il.Electromagnetic interference shieldingeffects of polyaniline-coated multi-wall carbon nanotubes/maghemite nanocomposites[J].Polym Bull,2012,68(2):561-573.
[8] WANG Lin-xia,LI Xin-gui,YANG Yu-liang.Preparation,properties and applications of polypyroles[J].Reactive and Functional Polymers,2001,47(2):125-139.
[9] UYGUN A,YAVUZ A G,SEN S,et al.Polythiophene/SiO2 nanocompositesprepared in the presence of surfactants and their application to glucose biosensing[J].Synthetic Met,2009,159(19/20):20-22.
[10] 武克忠,王新东,孟旭,等.直接甲醇燃料电池中聚苯胺载Pt电极的制备与性能测定[J].太阳能学报,2006,27(4):360-363.
[11] 周媛媛,余 ,李松,等.导电高分子材料聚苯胺的研究进展[J].化学推进与高分子材料,2007,5(6):14-19.
[12] BENITO D,GARCIÁ-JAREN J J,NAVARRO-LABOULAIS J,et al.Electrochemical behaviour of poly (neutral red) on an ITO electrode[J].J Electroanal Chem,1998,446(1/2):47-55.
[13] YANG Ru,RUAN Chuan-min,DAI Wei-lin,et al.Electropolymerization of thionine in neutral aqueous media and H2O2 biosensor based onpoly (thionine)[J].Electrochim Acta,1999,44(10):1585-1596.
[14] LIBUSE B,PETR H,JANA K,et al.The stability of polyaniline in strongly alkaline or acidic aqueous media[J].Polymer Degradation and Stability,2008,93(3):592-600.
[15] HAMNETT A,KENNEDY B J,WAGNER F E.Pt-Ru anodes for methanol electrooxidation:a ruthenium-99 Mössbauer study[J].J Catalysis,1990,124(1):30-40.
[16] HATCHETT D W,RANMALI W,JOHN M K.Reductionof PtCl2-4 and PtCl2-6 in polyaniline:catalytic oxidation of methanol at morphologically different composites[J].J Electroanal Chem,2006,593(1/2):203-210.
[17] SUN S G,BEWICK CLAVILIER A J.The mechanism of electrocatalytic oxidation of formic acid on Pt(100) and Pt(111) in sulphuric acid solution[J].J Electroanal Chem,1988,240(1/2):147-159.
[18] FUNGARO D A,OLIVEIRA-NETO A,LINARDI M.Electrocatalytic oxidation of methanol on platinum nanaparticles modified polyaniline electrode[J].Lat Am Appl Res,2007,37(3):85-90.
[19] HUANG Li-ming,CHEN Cheng-hou,WEN Ten-chin,et al.Effect of secondarydopants on electrochemical and spectroelectrochemical properties of polyaniline[J].Electrochim Acta,2006,51(13):2756-2764.
[1] 曾建强,何明基,李庆余,黄寒星,丁雪雪,毛全元,钟新仙. 中间相炭微球改性聚苯胺超级电容器电极材料研究[J]. 广西师范大学学报(自然科学版), 2017, 35(4): 84-90.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!
版权所有 © 广西师范大学学报(自然科学版)编辑部
地址:广西桂林市三里店育才路15号 邮编:541004
电话:0773-5857325 E-mail: gxsdzkb@mailbox.gxnu.edu.cn
本系统由北京玛格泰克科技发展有限公司设计开发